Magnesium sulfate was proposed to be leaching agent to deal with the ion-adsorption type rare earths ore to reduce or even eliminate ammonia?nitrogen emissions. The effects of temperature, particle size and stirring speed on rare earth leaching process and the leaching behaviors of the single rare earth element were investigated in order to reveal the rare earth leaching characteristics. Besides, the comparison of leaching effects between magnesium sulfate and ammonium sulfate was also studied. The results showed that the rare earth leaching process could be well described with inner diffusion control model and the apparent activation energy was 9.48 kJ/mol. The leaching behaviors of the single rare earth element were brought into correspondence with rare earths. Moreover, when the concentration of leaching agent was 0.20 mol/L, the rare earth leaching efficiency could all reach above 95% and the leaching efficiency of aluminum impurities could be restrained by 10% using magnesium sulfate compared with ammonium sulfate.
Sulfuric acid leaching process was applied to extracting rare earth（RE） from roasted ore of Dechang bastnaesite in Sichuan,China.The effect of particle size,stirring speed,sulfuric acid concentration and leaching temperature on RE extraction efficiency was investigated,and the leaching kinetics of RE was analyzed.Under selected leaching conditions,including particle size（0.074-0.100 mm）,sulfuric acid concentration 1.50 mol/L,mass ratio of liquid to solid 8 and stirring speed 500 r/min,the leaching kinetics analysis shows that the reaction rate of leaching process is controlled by diffusion through the product/ash layer which can be described by the shrinking-core model,and the calculated activation energy of 9.977 kJ/mol is characteristic for a diffusion-controlled process.