The modification of PAMAM( G =3 0) dendrimers was achieved by using aldehyde, benzyl chloride and trityl chloride as reaction agents, respectively. The complexes were synthesized simply by dropping TiCl 4 solution into the modified PAMAM dendrimers that were dissolved in certain solvent. The quantity of Ti contained in the complexes increased as the adding amount of TiCl 4 was increased. The polymerization of α methyl styrene catalyzed by the complexes was accomplished and it has shown that the complexes possessed catalytic function.
An ultrathin film with forth generation poly(aminoamine)(PAMAM) dendrimers (methyl quaternary ammonium salt) as polycation and poly(sodium \%p\% styrenesulfonate) (PSS) as polyainon was fabricated \%via\% sequential deposition. It shows that the step by step depositions carried out smoothly by monitoring with UV Vis spectrometer. The multilayer film is rather flat with a mean roughness of \{0.39 nm\} determined by AFM. The average thickness of a bilayer is \{5.0 nm\} obtained from XRD, which indicates that the dendrimers molecules were compressed and possess high flattening.