您的位置: 专家智库 > >

国家自然科学基金(50473031)

作品数:9 被引量:51H指数:5
相关作者:吴驰飞沈飞袁晓芳吴国章张梁更多>>
相关机构:华东理工大学更多>>
发文基金:国家自然科学基金上海市青年科技启明星计划更多>>
相关领域:化学工程理学更多>>

文献类型

  • 9篇中文期刊文章

领域

  • 6篇化学工程
  • 3篇理学

主题

  • 6篇配位
  • 4篇丁腈
  • 4篇丁腈橡胶
  • 4篇配位反应
  • 4篇橡胶
  • 4篇交联
  • 3篇酸铜
  • 3篇硫酸
  • 3篇硫酸铜
  • 2篇硫化
  • 1篇电子能
  • 1篇电子能谱
  • 1篇动力学
  • 1篇对苯二甲酸
  • 1篇对苯二甲酸乙...
  • 1篇液相
  • 1篇乙二醇酯
  • 1篇三氧化二锑
  • 1篇十溴二苯乙烷
  • 1篇配位键

机构

  • 8篇华东理工大学

作者

  • 8篇吴驰飞
  • 4篇沈飞
  • 4篇袁晓芳
  • 2篇李秋影
  • 2篇牟海艳
  • 2篇张梁
  • 2篇吴国章
  • 2篇郭卫红
  • 1篇宋治乾
  • 1篇曹元一
  • 1篇李慧

传媒

  • 3篇高分子学报
  • 2篇高等学校化学...
  • 1篇高分子通报
  • 1篇合成橡胶工业
  • 1篇塑料工业
  • 1篇Chines...

年份

  • 1篇2010
  • 2篇2009
  • 1篇2008
  • 3篇2007
  • 1篇2006
  • 1篇2005
9 条 记 录,以下是 1-9
排序方式:
COORDINATION CROSSLINKING OF NITRILE RUBBER FILLED WITH COPPER SULFATE PARTICLES被引量:4
2007年
By incorporating copper sulfate (CuSO4) particles into acrylonitrile butadiene rubber (NBR) followed by heat pressing, a novel vulcanization method is developed in rubber through the formation of coordination crosslinking. This method totally differs from traditional covalent or non-covalent vulcanization approaches of rubber. No other vulcanizing agent or additional additive is involved in this process. By analyzing the results of DMA, XPS and FT-IR, it is found that the crosslinking of CuSO4 particles filled NBR was induced by in situ coordination between nitrogen atoms of nitrile groups (-CN) and copper ions (Cu^2+) from CuSO4. SEM and EDX results revealed the generation of a core (CuSO4 solid particle)- shell (adherent NBR) structure, which leads to a result that the crosslinked rubber has excellent mechanical properties. Moreover, poly(vinyl chloride) (PVC) and liquid acrylonitrile-butadiene rubber (LNBR) were used as mobilizer to improve the coordination crosslinking of CuSO4/NBR. The addition of PVC or LNBR could lead to higher crosslink density and better mechanical properties of coordination vulcanization. In addition, crystal water in CuSO4 played a positive role to coordination crosslinking of rubber because it decreased the metal point of CuSO4 and promoted the metal ionization.
吴驰飞
关键词:COORDINATION
NBR/CuSO_4混合物的非液相配位交联反应被引量:8
2008年
采用示差扫描量热法(DSC),变温傅立叶转变红外光谱(FT-IR)和X射线光电子能谱(XPS)研究了丁腈橡胶/硫酸铜(NBR/CuSO4)混合物的非液相(聚合物熔融态)配位交联反应.DSC曲线上出现了多个放热峰,并随升温速率提高,峰值一致向高温方向移动;结合XPS和FT-IR的分析表明DSC曲线上的第一个放热峰对应于混合物中发生的铜离子与腈基的非液相配位反应;同时采用非等温法(Kissinger法)及Crane方程计算了NBR/CuSO4混合物非液相配位交联反应的表观活化能和反应级数.
牟海艳沈飞曹元一袁晓芳吴驰飞
关键词:反应动力学丁腈橡胶硫酸铜
配位交联的NBR/PVC合金的制备及表征被引量:15
2005年
The most common way of rubbers for obtaining high performance is vulcanization, by which the linear macromolecules are crosslinked into three-dimensional networks. The rubbers vulcanized by covalent bonds are serious pollutants. There has been an increasing interest in the novel rubbers crosslinked by supramolecular interactions such as hydrogen bonds and ionic bonds because of the supramolecular interactions are reversible and the crosslinked materials are likely to be recycled. In this paper, a series of novel NBR/PVC materials crosslinked with CuSO4 by coordinate bonds were prepared for the first time, and the produced materials have excellent mechanical properties. In this system, the coordinate bonds formed in situ during the heat press process. XPS and SEM results prove that there are really crosslinks by coordinated bonds between the polymers and the CuSO4 particles. The characterizations of mechanical properties, crosslink densities and the temperature of glass transition all showed that degree of crosslink and the performance of the coordinated materials could be adjusted controllably.
李慧沈飞吴驰飞
关键词:配位键交联X射线光电子能谱
(NBR/PVC)/CuSO_4复合材料中配位交联反应的研究被引量:9
2007年
采用差示扫描量热法(DSC)和傅立叶转换红外光谱(FT-IR)对丁腈橡胶/聚氯乙烯合金/无水硫酸铜((NBR/PVC)/CuSO4)混合物的配位交联反应进行了研究.结果表明,(NBR/PVC)/CuSO4共混物在升温过程中出现两个放热峰,分别归因于腈基(—CN)和CuSO4之间的配位交联反应和体系中NBR/PVC的自交联反应.通过对共混物配位交联反应动力学参数的计算发现,混合物中CuSO4含量的多少并未对体系配位交联反应的进行产生影响.同时共混物中PVC的存在促进了配位交联反应的进行,降低了铜离子(Cu2+)与—CN之间配位交联反应的表观活化能Ea.
沈飞吴驰飞
关键词:差示扫描量热法交联配位反应
结晶水对硫酸铜与丁腈橡胶之间配位交联反应的影响被引量:12
2006年
利用动态力学分析(DMA)、差示扫描量热分析(DSC)、扫描电子显微镜(SEM)、平衡溶胀法、力学性能测试等分析手段,通过研究五水硫酸铜(CuSO4.5H2O)填充的NBR考察了结晶水对CuSO4与NBR之间配位交联反应的影响.结果表明,结晶水的存在可以促进该配位交联反应.
袁晓芳吴国章吴驰飞
关键词:配位反应交联结晶水丁腈橡胶硫酸铜
硫酸铜含量对硫酸铜与丁腈橡胶之间配位交联反应的影响被引量:4
2007年
利用丁腈橡胶(NBR)的可配位侧基——腈基(—CN)与金属盐硫酸铜(CuSO4)的铜离子(Cu2+)之间的配位反应制备了一种配位交联CuSO4/NBR.影响该配位交联反应的因素众多,如热压温度、热压时间、增塑剂等等,考察了CuSO4含量对其的影响.通过X射线光电子能谱(XPS)、动态力学分析(DMA)、差示扫描量热分析(DSC)等手段对CuSO4与NBR之间的配位交联反应进行了分析,并对所得配位交联的CuSO4/NBR进行了交联密度及力学性能的测试.结果发现,随CuSO4含量的不断增加,CuSO4与NBR的配位交联程度逐渐增强,且所得配位交联CuSO4/NBR显示出从典型橡胶到韧性塑料再到脆性塑料的力学转变特性.另外,通过扫描电子显微镜(SEM)及X射线能谱仪(EDX)对材料的微观结构进行了分析,发现CuSO4在聚合物基体中不仅充当交联剂的角色,而且还起着增强填料的作用.
袁晓芳吴国章吴驰飞
关键词:配位反应交联丁腈橡胶硫酸铜
用Haake流变仪再生和硫化的废旧丁基橡胶的性能被引量:12
2010年
利用Haake流变仪的高温和剪切作用对废旧丁基橡胶(IIR)进行脱硫,考察了加工温度对再生胶脱硫程度、硫化再生胶力学性能的影响以及废旧IIR、再生胶和硫化再生胶的阻尼性能。结果表明,Haake流变仪能使废旧IIR达到脱硫的目的,当加工温度为200~320℃时,随着加工温度的提高,脱硫程度增大;与废旧IIR相比,再生IIR和硫化再生IIR的阻尼性能有很大程度提高。
张梁李秋影吴驰飞
关键词:脱硫HAAKE流变仪
抗滴落阻燃PET合金材料的研究被引量:4
2009年
研究环保型阻燃剂十溴二苯乙烷协同三氧化二锑对PET合金性能的影响,并利用防滴落剂聚四氟乙烯(PTFE)解决阻燃PET合金熔融滴落现象。通过TGA、UL-94垂直燃烧、极限氧指数(LOI)及成炭性考察了阻燃剂和防滴落剂对PET/弹性体阻燃性的影响,并对阻燃合金的力学性能进行了分析。结果表明,十溴二苯乙烷、三氧化二锑及防滴落剂的加入提高了材料的热稳定性,明显改善了合金的阻燃性,尤其加入PTFE后合金材料无熔融滴落现象,使PET合金的阻燃等级达V-0级。阻燃PET合金的力学性能随着PTFE的加入得到了改善。
张梁宋治乾李秋影郭卫红吴驰飞
关键词:聚对苯二甲酸乙二醇酯十溴二苯乙烷三氧化二锑阻燃
丁腈橡胶的配位硫化被引量:2
2009年
在丁腈橡胶中引入无机金属盐粒子,通过腈基与金属离子之间的固相配位反应来实现丁腈橡胶的配位硫化,创建了一个完全不同于传统硫磺硫化体系的新型非共价键配位交联的橡胶网络体系。同时制备了具有优异的力学性能的配位硫化橡胶材料,既可以作柔性的橡胶材料使用,也可以作为韧性、脆性的塑料材料使用。本文就影响配位交联反应的两个关键因素(金属盐粉末的粒径和丁腈橡胶的丙烯腈含量)进行了探讨,提出了提高配位硫化效率的办法(结晶水、增塑剂等)。
吴驰飞牟海艳沈飞郭卫红袁晓芳
关键词:非共价键金属配位硫化橡胶