The thermal decomposition of Zn-MPA complex was investigated under microwave irradiation. ZnO and ZnS nanocrystals could be obtained by decomposing Zn-MPA（3-mercaptopropionic acid） complex under different reaction conditions. It was found that both the pH value of the solution and the molar ratio of Zn2＋ and MPA can play an important role in the formation of ZnO and ZnS nanocrystals. MPA mainly acts as an S source or as a complexing agent. This study provides a new route for the controllable preparation of semiconductor nanocrystals.
Na1＋xV3O8 nanoribbon thin film was successfully fabricated by annealing the V2O5 xerogel film on sodium sili-cate glass substrate at 450℃. It has been identified that the amount of sodium ions diffused into the V2O5 xerogel film increases with the high temperature of annealing treatment. The sodium glass substrate serves as a limited sodium source to induce the transformation from V2O5 to Na1＋xV3O8.