Left-handed, coiled, 4,4＇-biphenylene bridged polybissilsesquioxane, tubular nanoribbons were prepared according to the published literature. After carbonization and removal of silica using HF aqueous solution, left-handed, coiled, carbonaceous, tubular nanoribbons were obtained. The left- handed, coiled, carbonaceous, tubular nanoribbons were characterized using field-emission scanning electron microscopy, transmission electron microscopy, powder X-ray diffraction, Raman spectropho- tometer, diffuse reflectance circular dichroism （DRCD）, and N2 adsorptions. Micropores were formed due to the removal of silica. The nitrogen BET surface area is 1727 m2/g. A broad, positive DRCD signal, identified at 400-800 rim, indicates the carbonaceous, tubular nanoribbons exhibit optical activity. The helical pitch is proposed to play an important role in the position of the DRCD signal.
Helical mesoporous silica nanorods were prepared using cetyltrimethylammonium bromide and achiral alcohols as the co-structure-directing agents. They were characterized using field-emission scanning electron microscopy, transmission electron microscopy, nitrogen sorptions, and small angle X-ray diffraction. The length of the silica nanorods increases with increasing the length of the alcohols. When n-heptanol and n-octanol were used, helical mesoporous silica nanorods with lamellar mesopores on the surfaces were obtained.
Yun Yue PuYi LiWei ZhuangMing ZhangBao Zong LiYong Gang Yang
Helical 1,2-ethylene-silica nanofibers with lamellar mesopores on the surfaces and twisted rod-like mesopores inside were prepared according to literature procedures. After carbonization, helical carbon/ silica nanofibers with lamellar mesopores on the surfaces and twisted rod-like micropores inside were obtained. The morphologies and pore architectures of the carbon]silica nanofibers were characterized using transmission electron microscopy, field-emission scanning electron microscopy, powder X-ray diffraction and N2 sorptions. Although the mesopores inside shrank into micropores, the helical nanostructure remained. Moreover, several carbon/silica nanofibers with lamellar mesopores on the surfaces and concentric circular micropores inside were also obtained. After being calcined in air, helical silica nanofibers with lamellar mesopores on the surfaces and twisted rod-like micropores inside were produced as well.