ZnO nanorod arrays （NRs） were synthesized on the fluorine-doped SnO2 transparent conductive glass （FTO） by a simple chemical bath deposition （CBD） method combined with alkali-etched method in potassium hydroxide （KOH） solution. X-ray diffraction （XRD）, scanning electron microscopy （SEM） and current-voltage （I-V） curve were used to characterize the structure, morphologies and optoelectronic properties. The results demonstrated that ZnO NRs had wurtzite structures, the morphologies and photovoltaic properties of ZnO NRs were closely related to the concentration of KOH and etching time, well-aligned and uniformly distributed ZnO NRs were obtained after etching with 0.1 mol/L KOH for 1 h. ZnO NRs treated by KOH had been proved to have superior photovoltaic properties compared with high density ZnO NRs. When using ZnO NRs etched with 0.1 mol/L KOH for 1 h as the anode of solar cell, the conversion efficiency, short circuit current and open circuit voltage, compared with the unetched ZnO NRs, increased by 0.71%, 2.79 mA and 0.03 V, respectively.
The crystalline structure and surface morphology of TiO2 semiconductor coating play an important role in the conversion efficiency of dye-sensitized solar cells. In order to obtain TiO2 coating with controllable morphology and high porosity, nanoporous TiO2 films were fabricated on conducting glass （FTO） substrates, Ti thin films （1.5-2 gin） were deposited on conducting glass （FTO） substrates via the DC sputtering method, and then electrochemically anodized in NH4F/ethylene glycol solution. The crystalline structure and surface morphology of the samples were characterized by X-ray diffraction （XRD） and field emission scanning electron microscopy （FESEM）, respectively. The influences of anodizing potential, electrolyte composition, and pH value on the surface morphology of nanoporous TiO2 films were extensively studied. The growth mechanism of nanoporous TiO2 films was discussed by current density variations with anodizing time. The results demonstrate that nanoporous TiO2 films with high porosity and three-dimensional （3D） networks are observed at 30 V, when the NH4F concentration in ethylene glycol solution is 0.3% （mass fraction） and the electrolyte pH value is 5.0.