The morphology,crystallization and elemental composition of cement hydration products in early age including Ca(OH)2,CSH gel,AFt and AFm were investigated by transmission electron microscopy(TEM).Compared with the results from SEM and XRD,the TEM method and its advantage in the investigation of early hydration products were discussed.The results showed that TEM method is more accurate and reliable than SEM in the investigation of early hydration products.The CSH gel was confirmed to be amorphous foil-like shape product with a lot of crumples in early hydration age.Its Ca/Si ratio is 1.3±0.2.The morphology difference of AFt and AFm was clarified.AFt and AFm are both poly-crystal with layered structure,composed of disordered nano crystal.The size of nano crystal is less than 20 nm.The difference of Ca/Si ratio results between SEM and TEM was investigated,and its reason was explained.
The changes of free solution amount, fluidity and the time-depended fluidity loss of cement paste were examined by varying the water-cement ratio and the dosages of superplasticizer. The distribution of solution and flocculation microstructure in flesh cement paste was observed with optical microscope. The change of free solution amount and its effect on the fluidity and bleeding of cement paste was studied. The results show that the adsorbed solution amount has a great influence on the com- patibility of cement-superplasticizer system, including the bleeding degree, the fluidity and the time-depended fluidity loss of cement paste. Superplasticizer increases the fluidity of cement paste by destroying the flocculated cement particle structure and increasing the amount of adsorbed solution. Polycarboxylate superplasticizer shows higher ability of adsorption than naphtha- lene superplasticizer. Over dosage of superplasticizer is not the primary cause of bleeding. The principle reason of bleeding is the high water-cement ratio and the insufficient enhancing ability of water adsorption of superplasticizer.