The effect of heating treatment on the trap level distribution in polyamide 66 film electret is studied by thermally stimulated depolarization current （TSDC） technique. For annealed polyamide 66, there are three trap levels that respectively originate from space charge trapped in amorphous phase, interphase and crystalline phase. There is one peak that originates from space charge trapped in amorphous phase for quenched one. Using multi-point method to fit the experimental curves, the detrapping current peaks can be separated and the trap depth is obtained. The shallower trap levels trapped in amorphous phase and interphase are obviously close to the deeper trap level trapped in crystalline phase for annealed polyamide 66 as the polarization temperature increases, while the trap level distribution remains unaffected by polarization temperature for quenched one.