A novel one-step protocol for the preparation of porous polyurea material （PPU） through precipitation polymerization of toluene diisocynate （TDI） is presented. The process is based on step polymerization of one single monomer, TDI, with water in water-acetone mixed solvent. PPU is obtained without need for any porogen or additives, and no any chemical modification on the outcome polymer is necessary. The morphology, pore size and size distribution of PPU are characterized by scanning electron microscope and BET nitrogen adsorption. Taking acid fuchsine （AF） and Congo Red as dye examples in wastewaters, their adsorption on, desorption from PPU and the reusability of PPU were tested. Experimental conditions for AF adsorption were optimized with regard to pH, adsorption time, AF concentration and amount of PPU. Results demonstrate that the as-prepared PPU is of high performance in dyes adsorption and recycled use. This work presents therefore a novel and attractive candidate for removal of anionic dyes from wastewaters.
Precipitation polymerizations of divinylbenzene（DVB） in pure supercritical carbon dioxide,and parallel runs with presence of a cosolvent were carried out.The results showed that use of acetone as the cosolvent contributed greatly to the formation of the monodisperse microspheres.PDVB microspheres,with obviously higher uniformity than reported up to date,were achieved using 6-7 mL of acetone in a reactor of 50 mL with DVB concentration of 0.4 mol/L under 16 MPa,a much lower pressure than previously reported without use of cosolvent.
Chun Sheng LiJing Cui Liang Xiao Li Zhu Xiang Zheng Kong