Using steel slag as a main raw material of ceramics is considered as a high value-added way. However, the relationship among the initial composition, ceramic microstructure, and macroscopic properties requires further study. In this paper, a series of ceramics with different slag ratios （0-70wt%） were designed, and the software FACTsage was introduced to simulate the formation of crystalline phases. The simulation results indicate that mullite is generated but drastically reduced at the slag ratios of 0-25wt%, and anorthite is the dominant crystalline phase in the slag content of 25wt%-45wt%. When the slag ratio is above 45wt%, pyroxene is generated more than anorthite. This is because increasing magnesium can promote the formation of pyroxene. Then, the formula with a slag content of 40wt% was selected and optimized. X-ray diffraction results were good consistent with the simulation results. Finally, the water absorption and bending strength of optimized samples were measured.
Lubrication and friction between the mould and strand are strongly influenced by mould oscillation, and play an important role in slab quality and operating safety during continuous casting processes. Investigation of mould oscillation is therefore essential for getting a better online control of the mould processes. A feasible approach for the development and optimization of mould oscillation was put forward, which combined online measurement of mould friction, design of negative oscillating parameters and evaluation for powder consumption. Three different control models including sinusoidal and non-sinusoidal oscillation for mould oscillations were developed to investigate and evaluate the effects of oscillation on mould friction and powder lubrication. For the purpose of investigating mould friction between mould and strand, online measurement was carried out on a slab continuous caster equipped with a hydraulic oscillator. Also the comparison of the mould friction in sinusoidal and non-sinusoidal mould oscillation was made for subsequent analysis. The industrial experiment result shows that the combination of inverse control model and non-sinusoidal oscillation mode will contribute to the proper powder consumption, leading to a suitable effect of friction force on strand surface, especially for high speed continuous casting. The proposed method provides reliable basis for guiding and optimizing mould oscillation among control models, sinusoidal oscillation and non-sinusoidal oscillation.
WANG Xu-dongYAO ManZHANG LiZHANG Xiao-bingCHEN Shao-hui