With mean yield（MY）criterion,an analytical solution of the collapse load for a defect-free pipe elbow under internal pressure is first obtained.It is a function of ratio of thickness to radius t0/r0,strain hardening exponent n,curvature influence factor mand ultimate tensile strength.The collapse load increases with the increase of m,and it is the same as the burst pressure of straight pipe if m=1is assumed.The MY-based solution is compared with those based on Tresca,Mises and twin shear stress（TSS）yield criteria,and the comparison indicates that Tresca and twin shear stress yield criteria predict a lower bound and an upper bound to the collapse load respectively.However,the MY-based solution lies just between the TSS and Tresca solutions,and almost has the same precision with the Mises solution.
In order to understand the effect of the solidification structure on the formability of ultra low carbon ferritic stainless steel （FSS） ,this work studies the ridging phenomenon and the deep-drawing property in detail and the research method was X-ray diffraction （XRD） and scanning electron microscope （SEM） technique. The result shows that the columnar grain specimen had a higher ridging height than the equiaxed grain specimen, which was mainly attributed to the formation of grain colonies in the columnar grain specimen. After final recrystallization annealing, the equiaxed grain specimen obtained a high-intensity T-fiber texture and an excellent deep-drawing property.
DU WeiJIANG LaizhuSUN QuansheYU HaifengQIN BinLIU Zhenyu