Wet etching has been widely used in defect evaluation for Ga-face GaN and surface roughness for N-face GaN dodecagonal pyramids has been fabricated on laser-lift-off N-face GaN by hot phosphor acid etching.The dodecagonal pyramid shows twelve facets including six{20-2-3}and six{22-4-5}planes.From cross-sectional TEM image,it is shown that the pyramid corresponds to the top of the edge dislocation.Compared with hexagonal pyramid-surface light emitting diodes(LEDs)etched by commonly used photoelectrochemical(PEC)process in KOH aqueous,the dodecagonal pyramid-surface LEDs show improved light extraction efficiency because of more facets,which effectively reduces the total internal reflection.
QI ShengLi,CHEN ZhiZhong,SUN YongJian,FANG Hao,TAO YueBin,SANG LiWen,TIAN PengFei,DENG JunJing,ZHAO LuBing,YU TongJun,QIN ZhiXin&ZHANG GuoYi State Key Laboratory for Artificial Microstructure and Mesoscopic Physics,School of Physics,Peking University,Beijing 100871,China
Non-polar a-plane （1120） GaN films have been grown on r-plane （1102） sapphire substrates by metal organic chemical vapour deposition. The influences of V/III ratio on the species diffusion anisotropy of a-plane GaN films were investigated by scanning electron microscopy, cathodoluminescence and high-resolution x-ray diffraction measurements. The anisotropy of a-plane GaN films may result from the different migration length of adatoms along two in-plane directions. V/III ratio has an effect on the growth rates of different facets and crystal quality. The stripe feature morphology was obviously observed in the film with a high V/III ratio because of the slow growth rate along the [1100] direction. When the V/III ratio increased from 1000 to 6000, the in-plane crystal quality anisotropy was decreased due to the weakened predominance in migration length of gallium adatoms.