Co68.15Fe4.35Si12.25B15.25 （at%） amorphous microwires with a smooth surface and a circular cross-section were fabricated by the glass-coated melt spinning method. Their mechanical properties were evaluated through tensile tests of the glass-coated amorphous mi-crowires, and their fracture reliability was estimated using two-and three-parameter Weibull analysis. X-ray diffraction and transmission electron microscopy results showed that these glass-coated Co-based microwires were mostly amorphous. The coated Co-based microwires exhibit a tensile strength of 1145 to 2457 MPa, with a mean value of 1727 MPa and a variance of 445 MPa. Weibull statistical analysis showed that the tensile two-parameter Weibull modulus of the amorphous microwires is 4.16 and the three-parameter Weibull modulus is 1.61 with a threshold value as high as 942 MPa. These results indicate that the fabricated microwires exhibit good tensile properties and fracture reliability, and thus appear to be good candidates for electronics reliability engineering applications.
Xiao-dong WangHuan WangHong-xian ShenFa-xiang QinDa-wei XingJing-shun LiuDong-ming ChenJian-fei Sun
Coaxially dielectric samples consisting of different packing ratios of glass-covered Fe73.5Si13.5B9Nb3Cu1 amorphous wires embedded in a paraffin wax matrix were fabricated, and the influence of short-wire packing ratio (3%-9% in mass fraction) and thickness (1-7 mm) on the microwave absorption properties was systematically investigated in microwave frequency range of 2-18 GHz. X-ray diffraction (XRD), differential scanning calorimetry (DSC), scanning electron microscopy (SEM) and scalar network analyzer (SNA) were used for characterizing microstructure and evaluating microwave absorption properties. Experimental results show the significant frequency (6-18 GHz) dependence of the complex relative permeability and permittivity. The reflection loss (RL) with different thickness and short-wire packing ratio reveals that the composite sample containing 7% exhibits better microwave absorption behavior with its minimum value of RL reaching-34 dB in thickness of 3 mm at 14 GHz. Therefore, it is significantly useful to develop microwire-dielectric materials with much wider absorption band for microwave absorption applications.